High-Rate and Cycling-Stable Nickel-Rich Cathode Materials with Enhanced Li(+) Diffusion Pathway

The nickel-rich LiNi0.7Co0.15Mn0.15O2 material was sintered by Li source with the Ni0.7Co0.15Mn0.15(OH)2 precursor, which was prepared via hydrothermal treatment after coprecipitation. The intensity ratio of I(110)/I(108) obtained from X-ray diffraction patterns and high-resolution transmission electronmicroscopy confirm that the particles have enhanced growth of (110), (100), and (010) surface planes, which supply superior inherent Li(+) deintercalation/intercalation. The electrochemical measurement shows that the LiNi0.7Co0.15Mn0.15O2 material has high cycling stability and rate capability, along with fast charge and discharge ability. Li(+) diffusion coefficient at the oxidation peaks obtained by cyclic voltammogram measurement is as large as 10(-11) (cm(2) s(-1)) orders of magnitude, implying that the nickel-rich material has high Li(+) diffusion capability.