Hierarchical Metal-Free Nitrogen-Doped Porous Graphene/Carbon Composites as an Efficient Oxygen Reduction Reaction
Bao Men1, Yanzhi Sun1, Mujie Li1
1National Fundamental Research Laboratory of New Hazardous Chemicals Assessment and Accident Analysis, Institute of Applied Electrochemistry, Beijing University of Chemical Technology , Beijing 100029, China.
Abstract:
Hierarchical nitrogen-doped porous graphene/carbon (NPGC) composites were fabricated by a simple and nontemplate method. The morphology characterizations demonstrate that reduced graphene oxide was successfully coated by the carbon derived from glucose, and a well-organized and interpenetrated hierarchical porous structure of NPGC was formed after pyrolysis at 950 °C. Notably, the prepared material, denoted as NPGC-950, has superlarge specific surface area (1510.83 m(2) g(-1)) and relatively high content percentage of pyridinic and graphitic nitrogen. As an efficient metal-free electrocatalyst, NPGC-950 exhibits a high onset potential (0.91 V vs RHE) and a nearly four-electron pathway for oxygen reduction reaction in alkaline solution as well as stronger methanol tolerance and better long-term durability than commercial Pt/C. In view of these excellent features, the obtained hierarchical N-doped metal-free porous carbon material is a promising catalyst for oxygen reduction reaction and could be widely applied in industry.