Adsorption behaviors of methyl orange dye on nitrogen-doped mesoporous carbon materials

A series of nitrogen-doped mesoporous carbon materials (NMC) with different nitrogen contents (from 9.1 to 11.3 wt.%) were prepared using urea and ammonia as economical nitrogen resources by sol-gel method. The NMC materials possessed high surface areas (from 659 m(2)/g to 912 m(2)/g) as well as large number of oxygen-containing and nitrogen-containing groups. The adsorption behaviors of NMC materials for anionic dye methyl orange (MO) were investigated, which are fit excellent for the Langmuir isothermal adsorption equation. All the materials exhibited high adsorption capacity for MO at room temperature. Their adsorption capacity can be adjusted by changing the nitrogen contents in NMC materials. Moreover, treating the NMC material at higher temperature can significantly improve the adsorption capacity for MO. According to the results of characterization, the main features of NMC materials, like large pore size and abundant basic nitrogen-containing groups on the surface, should be related to the excellent adsorption property for MO.