Enhanced sequestration of Cr(VI) by nanoscale zero-valent iron supported on layered double hydroxide by batch and
Guodong Sheng1, Jun Hu2, Hui Li3
1College of Chemistry and Chemical Engineering, College of Medical Science, Shaoxing University, Zhejiang 312000, PR China; Institute of Plasma Physics, Chinese Academy of Sciences, P.O. Box 1126, Hefei 230031, PR China.
Abstract:
Herein, the reduction of nanoscale zero-valent iron (NZVI) and adsorption of layered double hydroxides (LDH) to sequester Cr(VI) were well combined by the immobilization of NZVI onto LDH surface (NZVI/LDH). The characterization results revealed that LDH decreased NZVI aggregation and thus increased Cr(VI) sequestration. The batch results indicated that Cr(VI) sequestration by NZVI/LDH was higher than that of NZVI, and superior to the sum of reduction and adsorption. The LDH with good anion exchange property allowed the adsorption of Cr(VI), facilitating interfacial reaction by increasing the local concentration of Cr(VI) in the NZVI vicinity. X-ray absorption near edge structure (XANES) results indicated that Cr(VI) was almost completely reduced to Cr(III) by NZVI/LDH, but Cr(VI) was partly reduced to Cr(III) by NZVI with a trace of Cr(VI) adsorbed on corrosion products. The coordination environment of Cr from extended X-ray absorption fine structure (EXAFS) analysis revealed that LDH could be a good scavenger for the insoluble products produced during reaction. So, the insoluble products on NZVI could be reduced, and its reactivity could be maintained. These results demonstrated that NZVI/LDH exhibits multiple functionalities relevant to the remediation of Cr(VI)-contaminated sites.