Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...

Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...

In precipitation gravimetry, the precipitating agent should react specifically or selectively with the analyte. While a specific reagent reacts with the analyte alone, a selective reagent can react with a limited number of chemical species.
The obtained precipitate should be either a pure substance of known composition or easily converted to one by a simple process, such as ignition or drying. In addition, the precipitate should be insoluble and easily filterable. In general, filterability...

Ziegler–Natta polymerization is another form of addition or chain‐growth polymerization used for synthesizing linear polymers over branched polymers. The catalyst used for polymerization is the Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, who developed it in 1953. This catalyst is an organometallic complex of titanium tetrachloride and triethyl aluminum, with the active form of the catalyst being an alkyl titanium compound. Using the Ziegler–Natta...

The cationic polymerization mechanism consists of three steps: initiation, propagation, and termination. In the initiation step of the polymerization process, the π bond of a monomer gets protonated by the Lewis acid catalyst, which is formed from boron trifluoride and water. The protonation of the π bond generates a carbocation stabilized by the electron‐donating group. In the propagation step, the π bond of the second monomer acts as a nucleophile and attacks the...

The high insolubility of some precipitates can result in an unfavorable relative supersaturation. This can lead to colloidal particles with a large surface-to-mass ratio, where adsorption is promoted. For instance, in the precipitation of silver chloride, silver ions are adsorbed on the surface of the colloidal particles, forming a primary layer. This layer attracts ions of opposite charge (such as nitrate ions), forming a diffuse secondary layer of adsorbed ions. This electric double layer...