LiFePO4 nanoparticles enveloped in freestanding sandwich-like graphitized carbon sheets as enhanced remarkable...

A novel nanostructure where LiFePO4 nanoparticles are enveloped in sandwich-like carbon sheets as an enhanced cathode in lithium-ion batteries has successfully been synthesized for the first time. Compared to previous carbon-based nanocomposites, the achieved sandwich-like LiFePO4 nanocomposites exhibit totally different architecture, in which LiFePO4 nanoparticles are tightly entrapped between two carbon layers, instead of being anchored on the carbon sheet surfaces. In other words, the achieved sandwich-like LiFePO4 nanocomposite carbon layers are actually freestanding and can be operated and separated from each other. This is a great breakthrough in the design and synthesis of carbon-based functional materials. The obtained sandwich-like LiFePO4 nanocomposites present excellent electrochemical performance, which is rationally ascribed to the superb and unique structure and architecture. Of particular note is that the freestanding sandwich-like LiFePO4 nanocomposites exhibit enhanced cyclability and rate capability. At a high current density of 0.1 A g(-1), a stable specific capacity of approximately 168.5 mAh g(-1) can be delivered over 1000 cycles, and when the charge-discharge rates increase to 0.6, 2, 5 and 10 A g(-1), the specific capacities still survive at 149, 129, 114 and 91 mAh g(-1), respectively. Meanwhile, the sandwiched nanocomposite demonstrates a significantly improved low-temperature electrochemical energy storage performance. With respect to the excellent Li storage performance, and facility and reliability of production, the freestanding sandwich-like LiFePO4 nanocomposites are reasonably believed to have a great potential for multiple electrochemical energy storage applications.