Facile Fabrication of Bi2WO6/Ag2S Heterostructure with Enhanced Visible-Light-Driven Photocatalytic Performances

In this report, a novel photocatalyst based on Bi2WO6/Ag2S heterostructures was prepared by a 3-mercaptopropionic acid (MPA)-assisted route at room temperature. Compared to bare Bi2WO6 and Ag2S nanoparticles, the as-formed Bi2WO6/Ag2S heterostructures exhibit enhanced photocatalytic activity for the degradation of rhodamine B (Rh B) under visible-light irradiation. This kind of enhancement in the photocatalytic activity is considered to be the synergistic effects of both the effective electron-hole separation and expansion of the light-absorption range. The pH of the solution is of vital importance to the photocatalytic activity of the as-formed Bi2WO6/Ag2S heterostructures. Under low pH value, the photosensitization process is suppressed, while under higher pH value, the photosensitization process is favored. The mechanism of the photocatalytic process was proposed by the active-species-trapping experiments, indicating that the photogenerated holes (h(+)) play a crucial role in the degradation of Rh B under visible light. The enhanced photocatalytic performance of this heterostructure makes it a promising material for the treatment of dye-containing wastewater.