Role of anti-adhesive barriers following rotator cuff repair surgery: an experimental study

This experimental study investigates the effectiveness of expanded polytetrafluoroethylene (Dualmesh®, Gore Medical, Flagstaff, AZ, USA), sodium hyaluronate-carboxymethyl cellulose (Seprafilm®, Genzyme, Cambridge, MA, USA), and polysiloxane (silicone) as anti-adhesive barriers for inhibition of fibrosis in the subacromial area following rotator cuff repair.

Rabbit rotator cuff tenotomy and repair was conducted on 24 rabbits in 4 groups: control (Group A), Dualmesh® (Group B), Seprafilm® (Group C), and silicone (Group D). Anti-adhesive barrier materials were sutured over the repaired rotator cuff. Macroscopic and histological evaluations were made at the end of the sixth postoperative week.

Macroscopic evaluation revealed that minimal adhesion occurred in the control and silicone groups, while the Seprafilm® and Dualmesh® groups showed evidence of fibrosis. Microscopic evaluation revealed diffuse fibrosis and collagen accumulation in the Dualmesh® and Seprafilm® groups, whereas minimal collagen deposition and inflammatory cell reaction was found among the silicone and control groups. Significant differences were found between the silicone and Dualmesh® (p=0.001) and silicone and Seprafilm® groups (p=0.002), as well as between the control and Dualmesh® (p=0.002) and control and Seprafilm® groups (p=0.002).

Expanded polytetrafluoroethylene (ePTFE/Dualmesh®) and sodium hyaluronate carboxymethyl cellulose (SH-CMC/Seprafilm®) did not prevent or attenuate postoperative subacromial fibrosis following cuff tear repair. Nor did silicone prevent or attenuate fibrosis. More detailed research is needed for development of an effective anti-adhesive barrier for use after rotator cuff tear surgery.