Release of metal ions from round and rectangular NiTi wires
Arash Azizi1, Abdolreza Jamilian2, Francesca Nucci3
1Department of Oral and Maxillofacial Medicine, Tehran Dental Branch, Craniomaxillofacial Research Center, Islamic Azad University, Tehran, Iran.
Background:
The aim of this study was to evaluate the amount of nickel and titanium ions released from two wires with different shapes and a similar surface area.
Methods:
Forty round nickel-titanium (NiTi) arch wires with the diameter of 0.020 in. and 40 rectangular NiTi arch wires with the diameter of 0.016 × 0.016 in. were immersed in artificial saliva during a 21-day period. The surface area of both wires was 0.44 in.(2). Wires were separately dipped into polypropylene tubes containing 50 ml of buffer solution and were incubated and maintained at 37 °C. Inductively coupled plasma atomic emission spectrometry (ICP-AES) was used to measure the amount of ions released after exposure lengths of 1 h, 24 h, 1 week, and 3 weeks. Repeated measures ANOVA and Tukey tests were used to evaluate the data.
Results:
The results indicated that the amount of nickel and titanium concentrations was significantly higher in the rectangular wire group. The most significant release of all metals was measured after the first hour of immersion. In the rectangular wire group, 243 ± 4.2 ng/ml of nickel was released after 1 h, while 221.4 ± 1.7 ng/ml of nickel was released in the round wire group. Similarly, 243.3 ± 2.8 ng/ml of titanium was released in the rectangular wire group and a significantly lower amount of 211.9 ± 2.3 ng/ml of titanium was released in the round wire group.
Conclusions:
Release of metal ions was influenced by the shape of the wire and increase of time.
Related Concept Videos
02:32Bonding in Metals
01:08Electrodeposition
Electrodeposition can...
01:19Conductors and Insulators
Most metals are conductors. Their atomic configuration is such that one or more electron(s) are loosely bound to the nucleus in each atom. Thus, a sea of mobile electrons are available in them, known as free electrons. Their easy...
01:15Charging Conductors By Induction
Generally, conductors like metals do not allow any excess charge to be present on them. Any excess charge added to metals easily flows away, for example, when a metal is placed on the Earth. This process is called earthing.
However, conductors can be charged by a process called induction. For example, consider charging a...
02:47Voltaic/Galvanic Cells
Spontaneous redox reactions occur abundantly in nature. The chemical reaction occurring in a disposable AA battery powering our remote controls is one such example of a spontaneous redox reaction. Another example is the immersion of coiled copper wire into an aqueous silver nitrate solution. The reaction shows a gradual, visually impressive color change from colorless to bright blue and the formation of a grey precipitate on the copper wire. In this experiment,...
02:51Metal-Ligand Bonds
In these complexes, transition metals form coordinate covalent bonds, a kind of Lewis acid-base interaction in which both of the electrons in the bond are contributed by a donor (Lewis base) to an electron acceptor (Lewis acid). The Lewis acid in...