PHYSICOCHEMICAL CHARACTERIZATION OF LYOPHILIZED BOVINE BONE GRAFTS
Carlos Roberto Galia1, André Luis Lourenço2, Ricardo Rosito3
1Contracted Physician in the Hip Group and Technical Coordinator of the Tissue Bank, HCPA, Porto Alegre, RS; MSc in Surgery from UFRGS, Porto Alegre, RS, Brazil.
Unlabelled:
To evaluate the physicochemical characteristics of lyophilized bovine grafts manufactured on a semi-industrial scale (Orthogen; Baumer S/A*) in accordance with a protocol previously developed by the authors.
Methods:
The lyophilized bovine bone grafts were characterized by means of scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffractometry (XRD), thermogravimetric (TG) analysis, differential exploratory scanning calorimetry (DSC) and Fourier-transform infrared (FT-IR) spectroscopy.
Results:
Ca was the main component (60%) found in the samples, followed by P (28%) and O (5%). The mean (sd) pore size was 316 μm (146.7), ranging from 91.2 to 497.8 μm, and 333.5 μm (304.8), ranging from 87.2 to 963.9 μm, at 50x and 150x magnification, respectively. The hydroxyapatite peaks were at 26°C and 32°C, and mass losses were observed between 250°C and 640°C, corresponding to organic material and water. Two temperature transitions (45.67°C and 91.89°C) showed denaturation of type 1 collagen and dehydration of hydroxyapatite.
Conclusion:
The physicochemical assessment of lyophilized bovine bone grafts in accordance with the protocol developed at semi-industrial scale confirmed that this product presents excellent biocompatibility, with characteristics similar to natural bone.