Effects of maximum aggregate size on UPV of brick aggregate concrete

Tarek Uddin Mohammed1, Aziz Hasan Mahmood1

  • 1Department of Civil and Environmental Engineering, Islamic University of Technology, Gazipur 1704, Bangladesh.

Ultrasonics
|April 17, 2016
PubMed

Keywords:
Compressive strengthConcreteImage analysisInterfacial transition zoneMaximum aggregate sizeYoung’s modulus

More Related Videos

Experimental Protocol to Investigate Particle Aerosolization of a Product Under Abrasion and Under Environmental Weathering07:47

Experimental Protocol to Investigate Particle Aerosolization of a Product Under Abrasion and Under Environmental Weathering

Published on: September 16, 2016

7.9K
Determination of Aggregate Surface Morphology at the Interfacial Transition Zone ITZ08:59

Determination of Aggregate Surface Morphology at the Interfacial Transition Zone ITZ

Published on: December 16, 2019

8.8K

Related Concept Videos

Maximum Size of Aggregate01:12

Maximum Size of Aggregate

The maximum size of aggregate is defined as the aperture of the sieve retaining 15 percent or more of the particles present in the aggregate sample. The aggregate's maximum size impacts the concrete's water requirement, workability, and strength. Larger aggregates reduce the surface area needing cement paste coverage, which can lower water needs, thereby allowing a decrease in the water-to-cement ratio when the desired workability and richness of the mix are to be maintained, which can...
817
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
531
Unsoundness of Aggregate due to Volume Change01:26

Unsoundness of Aggregate due to Volume Change

Unsoundness in aggregates due to volume changes is primarily caused by the physical alterations aggregates undergo, such as freezing and thawing, thermal changes, and wetting and drying. Unsound aggregates, when subjected to these changes, result in volume change upon disintegration. This, in turn, contributes to the deterioration of concrete, including scaling, pop-outs, and cracking. Particular types of aggregates, such as porous flints, cherts, and those containing clay minerals, are...
434
Porosity and Absorption of Aggregate01:20

Porosity and Absorption of Aggregate

Aggregates contain pores of varying sizes; while some are completely enclosed within the particles, others open onto the surface, allowing water to penetrate. The porosity of aggregates is a major factor contributing to the overall porosity of concrete, given that aggregates constitute about three-quarters of concrete's volume.
When all pores in an aggregate are filled with water, the aggregate is considered saturated and surface-dry. If left in dry air, water will evaporate until the...
894
Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
698
Impact Strength of Concrete01:21

Impact Strength of Concrete

Impact strength in concrete is a critical measure that reflects the material's capability to endure the forces applied during pile driving and when supporting machinery foundations that experience impulsive loads. It is also essential when handling precast concrete components to prevent accidental damage. The impact strength is assessed by observing the concrete's resistance to repeated impacts and energy absorption capacity. A key indicator of significant damage to concrete is when it...
694