Two-Dimensional Organic Single Crystals with Scale Regulated, Phase-Switchable, Polymorphism-Dependent, and Amplified
Zhenyu Zhang1, Xiaoxian Song1, Shipan Wang1
1State Key Laboratory of Supramolecular Structure and Materials, College of Chemistry, Jilin University , 2699 Qianjin Avenue, Changchun 130012, P. R. China.
Abstract:
The successful preparation of two-dimensional (2D) single crystals can promote the development of organic optoelectronic devices with excellent performance. A Schiff base compound salicylidene(4-dimethylamino)aniline with aggregation induced emission (AIE) property was employed as the building block to fabricate 2D thin single crystal plates with scales from around 50 μm to 1.5 cm. Yellow and red emissive polymorphs were concomitantly obtained during crystallization. The single-crystal-to-single-crystal (SC-to-SC) transformation from yellow polymorph to red one was demonstrated. Furthermore, both polymorphs exhibited amplified spontaneous emission (ASE) properties. Interestingly, the red polymorph displayed size-dependent ASE characteristics. The larger red polymorph showed near-infrared ASE with maximum at 706 nm, whereas the smaller one presented red ASE with maximum at 610 nm. These results suggest that the different scale single crystalline thin films with perfect optoelectronic properties may be fabricated by using the organic molecules with 2D assembly feature.