Microleakage under ceramic flash-free orthodontic brackets after thermal cycling
Objective:
To compare microleakage under 3M Unitek's APC Flash-Free Adhesive Coated System bracket and the APC PLUS Adhesive Coated System bracket after thermal cycling.
Materials And Methods:
Forty freshly extracted human maxillary premolars were randomly divided into two groups and bonded with either a Flash-Free bracket or a PLUS bracket. After bonding, the samples were incubated in a water bath at 37°C for 24 hours and thermocycled for 5000 cycles between 5°C and 50°C. All teeth were immersed in a 2% methylene blue solution for 24 hours, embedded in acrylic and sectioned in a buccolingual direction at approximately the center of the bracket. Microleakage was observed at the enamel-adhesive interface from the occlusal and gingival margins of the bracket base. Statistical analysis was conducted using the Mann-Whitney U-test.
Results:
The median microleakage was higher in the Flash-Free group, but the difference between the two groups was not statistically significant (P > .05).
Conclusion:
In a laboratory setting, there is no significant difference between the extent of microleakage under the APC Flash-Free Adhesive Coated System bracket and the APC PLUS Adhesive Coated System bracket after thermal cycling.