Characterization of Electrode Materials for Lithium Ion and Sodium Ion Batteries Using Synchrotron Radiation Techniques
Published on: November 11, 2013
Efficient plasma-enhanced method for layered LiNi1/3Co1/3Mn1/3O2 cathodes with sulfur atom-scale modification for
Qianqian Jiang1, Ning Chen, Dongdong Liu
1SZU-NUS Collaborative Innovation Center for Optoelectronic Science & Technology, Key Laboratory of Optoelectronic Devices and Systems of Ministry of Education and Guangdong Province, College of Optoelectronic Engineering, Shenzhen University, Shenzhen 518060, China. hzhang@szu.edu.cn.
Abstract:
In order to improve the electrochemical performance of LiNi1/3Co1/3Mn1/3O2 as a lithium insertion positive electrode material, atom-scale modification was realized to obtain the layered oxysulfide LiNi1/3Co1/3Mn1/3O2-xSx using a novel plasma-enhanced doping strategy. The structure and electrochemical performance of LiNi1/3Co1/3Mn1/3O2-xSx are investigated systematically, which confirms that the S doping can make the structure stable and benefit the electrochemical performance. The phys-chemical characterizations indicate that oxygen atoms in the initial LiNi1/3Co1/3Mn1/3O2 have been partially replaced by S atoms. It should be pointed out that the atom-scale modification does not significantly alter the intrinsic structure of the cathode. Compared to the pristine material, the LiNi1/3Co1/3Mn1/3O2-xSx shows a superior performance with a higher capacity (200.4 mA h g(-1)) and a significantly improved cycling stability (maintaining 94.46% of its initial discharge capacity after 100 cycles). Moreover, it has an excellent rate performance especially at elevated performance, which is probably due to the faster Li(+) transportation after S doping into the layered structure. All the results show that the atom-scale modification with sulfur atoms on LiNi1/3Co1/3Mn1/3O2, which significantly improved the electrochemical performance, offers a novel anionic doping strategy to realize the atom-scale modification of electrode materials to improve their electrochemical performance.