Comparative failure load values of acrylic resin denture teeth bonded to three different heat cure denture base
Sumit Singh Phukela1, Amit Dua2, Mahima Dua3
1Department of Prosthodontics, Faculty of Dental Science, SGT University, Gurgaon, Haryana, India.
Aim And Objectives:
Acrylic teeth are used for fabrication of dentures. Debonding of tooth - denture base bond is routine problem in dental practice. The aim of this study was to comparatively evaluate failure load of acrylic resin denture teeth bonded to three different heat resin.
Materials And Methods:
Four groups were created out of test samples central incisors (11). Group I: Control, whereas Group II, Group III and Group IV were experimental groups modified with diatoric hole, cingulum ledge lock and Teeth modified with both diatoric hole and cingulum ledge lock, respectively. These test specimens with 3 teeth (2 central [11, 21] and 1, lateral [12] incisors) positioned imitating arrangement of teeth in the conventional denture, prepared by three different heat cure materials (DPI, Trevalon, Acralyn-H). A shear load was applied at cingulum of central incisor (11) at 130° to its long axis using universal tester at a cross head speed of 5 mm/min until failure occurred. Failure load test was conducted and statistical analysis was performed using SPSS 16 software package (IBM Company, New York, U.S).
Results:
Highest failure load was seen in Group IV specimens, prepared by Trevalon but did not significantly differ from that of DPI.
Conclusion:
The failure load of bonding denture teeth to three different heat cure materials was notably affected by modifications of ridge lap before processing. The specimens with a combination of diatoric hole and cingulum ledge lock, prepared by Trevalon showed highest failure load but did not significantly vary from that of DPI. The control group prepared by Acralyn-H showed lowest failure load but did not significantly differ from that of DPI.