Surface modification of electrospun PLGA scaffold with collagen for bioengineered skin substitutes

In skin tissue engineering, surface feature of the scaffolds plays an important role in cell adhesion and proliferation. In this study, non-woven fibrous substrate based on poly (lactic-co-glycolic acid) (PLGA) (75/25) were hydrolyzed in various concentrations of NaOH (0.05N, 0.1N, 0.3N) to increase carboxyl and hydroxyl groups on the fiber surfaces. These functional groups were activated by EDC/NHS to create chemical bonding with collagen. To improve bioactivity, the activated substrates were coated with a collagen solution (2mg/ml) and cross-linking was carried out using the EDC/NHS in MES buffer. The effectiveness of the method was evaluated by contact angle measurements, porosimetry, scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), tensile and degradation tests as well as in vitro cell attachment and cytotoxicity assays. Cell culture results of human dermal fibroblasts (HDF) and keratinocytes cell line (HaCat) revealed that the cells could attach to the scaffold. Further investigation with MTT assay showed that the cell proliferation of HaCat significantly increases with collagen coating. It seems that sufficient stability of collagen on the surface due to proper chemical bonding and cross-linking has increased the bioactivity of surface remarkably which can be promising for bioengineered skin applications.