Multi-Scale Modification of Metallic Implants With Pore Gradients, Polyelectrolytes and Their Indirect Monitoring In vivo
Published on: July 1, 2013
Investigation of enhanced hemocompatibility and tissue compatibility associated with multi-functional coating based
Jingan Li1, Kun Zhang2, Wenyong Ma1
1Key Laboratory for Advanced Technologies of Materials, Ministry of Education, School of Material Science and Engineering, Southwest Jiaotong University, Chengdu 610031, People's Republic of China;
Abstract:
The biocompatibility of cardiovascular devices has always been considered crucial for their clinical efficacy. Therefore, a biofunctional coating composed of Type IV collagen (CoIV) and hyaluronan (HA) was previously fabricated onto the titanium (Ti) substrate for the application of promoting vascular smooth muscle cell contractile phenotype and improving surface endothelialization. However, the anti-inflammation property, blood compatibility and in vivo tissue compatibility of the HA/CoIV coating, as paramount consideration of cardiovascular materials surface coating, have not been investigated. Thus, in this study, the three crucial properties of the HA/CoIV coating were tested. The platelet adhesion/activation test and the dynamic whole blood experiment implied that the HA/CoIV coating had better blood compatibility compared with Ti substrate and pure CoIV coating. The macrophage adhesion/activation and inflammatory cytokine release (tumor necrosis factor-alpha and interleukin-1) results indicated that the HA/CoIV coating could significantly improve the anti-inflammation property of the Ti substrate. The in vivo implantation of SD rats for 3 weeks' results demonstrated that the HA/CoIV coating caused milder tissue response. All these results suggested that the multi-functional HA/CoIV coating possessed good biocompatibility. This research is anticipated to be potentially applied for the surface modification of cardiovascular stents.