Ascorbic Acid-Assisted Synthesis of Mesoporous Sodium Vanadium Phosphate Nanoparticles with Highly sp(2) -Coordinated...

Herein, mesoporous sodium vanadium phosphate nanoparticles with highly sp(2) -coordinated carbon coatings (meso-Na3 V2 (PO4 )3 /C) were successfully synthesized as efficient cathode material for rechargeable sodium-ion batteries by using ascorbic acid as both the reductant and carbon source, followed by calcination at 750 °C in an argon atmosphere. Their crystalline structure, morphology, surface area, chemical composition, carbon nature and amount were systematically explored. Following electrochemical measurements, the resultant meso-Na3 V2 (PO4 )3 /C not only delivered good reversible capacity (98 mAh g(-1) at 0.1 A g(-1) ) and superior rate capability (63 mAh g(-1) at 1 A g(-1) ) but also exhibited comparable cycling performance (capacity retention: ≈74 % at 450 cycles at 0.4 A g(-1) ). Moreover, the symmetrical sodium-ion full cell with excellent reversibility and cycling stability was also achieved (capacity retention: 92.2 % at 0.1 A g(-1) with 99.5 % coulombic efficiency after 100 cycles). These attributes are ascribed to the distinctive mesostructure for facile sodium-ion insertion/extraction and their continuous sp(2) -coordinated carbon coatings, which facilitate electronic conduction.