Ionic Liquid-Derived Imidazolium Cation Linkers for the Layer-by-Layer Assembly of Polyoxometalate-MWCNT Composite...

Imidazolium cations derived from ionic liquids were demonstrated as effective linker molecules for the layer-by-layer (LbL) deposition of polyoxometalates (POMs) to increase the charge storage of multi-walled carbon nanotube (MWCNT) electrodes. MWCNTs modified with GeMo12O40(4-) (GeMo12) via an imidazolium cation linker demonstrated highly reversible redox reactions and a capacitance of 84 F cm(-3), close to 4 times larger than bare CNT. Compared to CNT-GeMo12 composites fabricated with a conventional polyelectrolyte linker poly(diallyldimethylammonium chloride), (PDDA), the imidazolium cations resulted in lower POM loading, but higher conductivity and in turn superior performance at fast charge-discharge conditions. A polymerized imidazolium linker (PIL) was also synthesized based on the ethyl-vinyl-imidazolium monomer. CNT-GeMo12 composites fabricated with this PIL achieved high POM loading comparable to PDDA, while still maintaining the good conductivity and high rate capabilities shown by the monomer imidazolium units. The high conductivity imparted by the PIL is especially valuable for the fabrication of multilayer POM composites. Dual-layer GeMo12 O40(4-)-SiMo12O40(4-) (GeMo12-SiMo12) electrodes built with this PIL demonstrated a combined contribution of the individual POMs resulting in a capacitance of 191 F cm(-3), over nine times larger than bare MWCNT. The PIL dual layer composites also maintained 72% of this capacitance at a fast rate of 2 V s(-1), compared to just over 50% retention for similar electrodes fabricated with PDDA.