Assessment of post-contamination treatments affecting different bonding stages to dentin

To assess the effect of cleansing treatments following saliva and blood contamination at different bonding stages to dentin.

Labial surfaces of 168 permanent maxillary central incisors were ground flat exposing superficial dentin. Specimens were divided into: uncontaminated control (A), contamination after etching (B), contamination after adhesive application (C), contamination after adhesive polymerization (D). Groups were further subdivided according to cleansing treatments into: rinsing (B1, C1, D1), re-etching (B2, D3), sodium hypochlorite application (B3), ethyl alcohol application (C2), acetone application (C3), rinsing and rebonding (D2), re-etching and rebonding (D4). Composite microcylinders were bonded to treated substrates and shear loaded micro-shear bond strength (μSBS) until failure and treated surfaces were examined with scanning electron microscope. Debonded surfaces were classified as adhesive, cohesive or mixed failure. The data were analyzed using one-way ANOVA and Tukey's post hoc test.

The μSBS values were ranked as follow; Group B: A > B3 > B2 > B1 > B, Group C: A > C3 > C2 > C1 > C, Group D: A > D4 > D1 = D2 ≥ D3. Debonded surfaces showed adhesive failure in Group B while cohesive failure in Groups C and D.

Cleansing treatments differ according to bonding step; re-etching then rebonding suggested if etched substrate or polymerized adhesive were contaminated while acetone application decontaminated affected unpolymerized adhesive.