Emergence of superconductivity in (NH3)yMxMoSe2 (M: Li, Na and K)

We report syntheses of new superconducting metal-doped MoSe2 materials (MxMoSe2). The superconducting MxMoSe2 samples were prepared using a liquid NH3 technique, and can be represented as '(NH3)yMxMoSe2'. The Tcs of these materials were approximately 5.0 K, independent of x and the specific metal atom. X-ray diffraction patterns of (NH3)yNaxMoSe2 were recorded using polycrystalline powders. An increase in lattice constant c showed that the Na atom was intercalated between MoSe2 layers. The x-independence of c was observed in (NH3)yNaxMoSe2, indicating the formation of a stoichiometric compound in the entire x range, which is consistent with the x-independence of Tc. A metallic edge of the Fermi level was observed in the photoemission spectrum at 30 K, demonstrating its metallic character in the normal state. Doping of MoSe2 with Li and K also yielded superconductivity. Thus, MoSe2 is a promising material for designing new superconductors, as are other transition metal dichalcogenides.