Hydrothermal Synthesis and Luminescent Properties of Eu3+ Doped Sr3Al2O6 Phosphor for White LED

Eu3+ ions doped Sr3Al2O6 phosphors were successfully synthesized via a hydrothermal method. The precursor was prepared by low temperature hydrothermal method using ammonia as both alkaline source and precipitator. Then the final product was obtained by high temperature sintering. In addition, the structures, morphologies, and luminescent properties of as-prepared products were thoroughly characterized by X-ray powder diffraction (XRD), Scanning electron microscopy (SEM), Fluorescence spectroscopy (PL). XRD shown a single phase Sr3Al2O6 prepared by a facile hydrothermal method at 250 °C for 10 h. In the PL spectra of as-prepared samples, the optimal value of Eu3+ concentration is 2 mol%. From the fluorescent spectra, the emission peaks of Sr3Al2O6: Eul+ phosphors are centered at around 591 nm, and the excitation peaks are centered at around 233 nm, 323 nm, 394 nm, and 468 nm, respectively, which were assigned to the characteristic transition of Eu3+ ions. The influence of ammonia, and the synthesis temperature on the luminescent properties of Sr3Al206: Eu3+ phosphors were studied in detail. The alkaline earth aluminates luminescent materials activated by rare earth ions have good prospects in the field of new-generation light sources.