Tuning Oxide Properties by Oxygen Vacancy Control During Growth and Annealing
06:44

Tuning Oxide Properties by Oxygen Vacancy Control During Growth and Annealing

Published on: June 9, 2023

3.9K

Effect of Oxygen-deficiencies on Resistance Switching in Amorphous YFe0.5Cr0.5O3-d films

Xianjie Wang1, Chang Hu1, Yongli Song1

  • 1Department of Physics, Harbin Institute of Technology, Harbin 150001, China.

Scientific Reports
|July 26, 2016
PubMed

More Related Videos

Bulk and Thin Film Synthesis of Compositionally Variant Entropy-stabilized Oxides09:41

Bulk and Thin Film Synthesis of Compositionally Variant Entropy-stabilized Oxides

Published on: May 29, 2018

10.1K
Niobium Oxide Films Deposited by Reactive Sputtering: Effect of Oxygen Flow Rate08:23

Niobium Oxide Films Deposited by Reactive Sputtering: Effect of Oxygen Flow Rate

Published on: September 28, 2019

8.0K

Related Concept Videos

Imperfections in Crystal Structure: Stoichiometric Point Defects01:26

Imperfections in Crystal Structure: Stoichiometric Point Defects

Schottky defects arise when some lattice points in a crystal, such as those in NaCl, remain unoccupied, creating lattice vacancies without disturbing the overall electrical neutrality of the crystal. This defect is common in ionic crystals where the positive and negative ions are similar in size, as seen in sodium chloride and cesium chloride. The presence of Schottky defects enables the crystal to conduct electricity to a small extent through an ionic mechanism. Electric fields cause nearby...
53
Imperfections in Crystal Structure: Non-Stoichiometric Defects01:29

Imperfections in Crystal Structure: Non-Stoichiometric Defects

Non-stoichiometric defects refer to a type of defect in the crystal structure of a compound where the ratio of its constituent elements deviates from the ideal stoichiometric ratio. There are two main types of non-stoichiometric defects: metal excess defects and metal deficiency defects.Metal excess defects occur when there is a slight surplus of metal ions than what is required by the stoichiometric ratio of the compound. For example, heating a sodium chloride crystal in sodium vapor results...
31