Anodic Ag/TiO2 nanotube array formation in NaOH/fluoride/ethylene glycol electrolyte as a photoanode for
Nyein Nyein1,2, Wai Kian Tan3, Go Kawamura2
1Green Electronics Nanomaterials Group, School of Materials and Mineral Resources Engineering Campus, Universiti Sains Malaysia, 14300 Nibong Tebal, Penang, Malaysia.
Abstract:
Self-organized, 23 μm-thick anodic TiO2 nanotube (TNT) arrays were formed in sodium hydroxide/fluoride/ethylene glycol (EG) electrolyte at 60 V for 60 min. The presence of sodium hydroxide (NaOH) in the fluoride/EG electrolyte accelerates the formation of the TiO2 nanotube arrays. The anodic film was then decorated with silver nanoparticles (Ag NPs) by the photodeposition process and used as a photoanode in a rear-side-illuminated dye-sensitized solar cell. The Ag NPs decorated TNT arrays, with the former having diameters of 10-30 nm formed from 0.2 M of Ag-precursor solution and exhibiting the highest photoconversion efficiency (η) of 3.7% and a short-circuit current density of 12.2 mA cm(-2) compared to η = 3% and short-circuit current density of 9.1 mA cm(-2) for a sample without Ag NPs. The increase in η is thought to be due to the surface plasmon resonance and excess electrons from the nanoparticles.
More Related Videos
12:47Preparation and Use of Photocatalytically Active Segmented Ag|ZnO and Coaxial TiO2-Ag Nanowires Made by Templated Electrodeposition
Published on: May 2, 2014
11:26Integrating a Triplet-triplet Annihilation Up-conversion System to Enhance Dye-sensitized Solar Cell Response to Sub-bandgap Light
Published on: September 12, 2014