Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production
Published on: December 6, 2021
Ionic-Liquid-Modified Hybrid Materials Prepared by Physical Vapor Codeposition: Cobalt and Cobalt Oxide Nanoparticles
Sascha Mehl1, Tanja Bauer1, Olaf Brummel1
1Lehrstuhl für Physikalische Chemie II, Friedrich-Alexander-Universität Erlangen-Nürnberg , Egerlandstraße 3, D-91058 Erlangen, Germany.
Abstract:
The synthesis of ionic-liquid-modified nanomaterials has attracted much attention recently. In this study we explore the potential to prepare such systems in an ultraclean fashion by physical vapor codeposition (PVCD). We codeposit metallic cobalt and the room-temperature ionic liquid (IL) 1-ethyl-3-methylimidazolium trifluoromethanesulfonate [C1C2Im][OTf] simultaneously onto a Pd(111) surface at 100 K. This process is performed under ultrahigh-vacuum (UHV) conditions in the presence of CO, or in the presence of O2 and CO. We use time-resolved (TR) and temperature-programmed (TP) infrared reflection absorption spectroscopy (IRAS) to investigate the formation and stability of the IL-modified Co deposits in situ during the PVD-based synthesis. CO is used as a probe molecule to monitor the growth. After initial growth of flat Co films on Pd(111), multilayers of Co nanoparticles (NPs) are formed. Characteristic shifts and intensity changes are observed in the vibrational bands of both CO and the IL, which originate from the electric field at the IL/Co interface (Stark effect) and from specific adsorption of the [OTf](-) anion. These observations indicate that the Co aggregates are stabilized by mixed adsorbate shells consisting of CO and [OTf](-). The CO coverage on the Co particle decreases with increasing temperature, but some CO is preserved up to the desorption temperature of the IL (370 K). Further, the IL shell suppresses the oxidation of the Co NPs if oxygen is introduced in the PVCD process. Only chemisorbed oxygen is formed at oxygen partial pressures that swiftly lead to formation of Co3O4 in the absence of the IL (5 × 10(-6) mbar O2). This chemisorbed oxygen is found to destabilize the CO ligand shell. The oxidation of Co is not suppressed if IL and Co are deposited sequentially under otherwise identical conditions. In this case we observe the formation of fully oxidized cobalt oxide particles.