Liquid-Phase Synthesis of Ba2V2O7 Phosphor Powders and Films Using Immiscible Biphasic Organic-Aqueous Systems

A liquid-phase synthesis of inorganic phosphor materials at a moderate temperature was proposed by using immiscible liquid-liquid biphasic systems. A self-activated Ba2V2O7 phosphor was actually synthesized from vanadium alkoxide dissolved in an organic solution and barium acetate in an aqueous solution. A mild hydrolysis reaction of the alkoxide started at the organic-inorganic interface, and an intermediate compound, Ba(VO3)2·H2O, was initially formed. Ba2V2O7 powders were then obtained by the conversion from Ba(VO3)2·H2O promoted in the aqueous solution. Ba2V2O7 films were obtained on surface-modified silica glass substrates through the similar chemical reactions. Factors such as the surface state of substrates, the kind of organic solvents, and the volume of aqueous solutions were examined to improve the film deposition behavior. The resultant Ba2V2O7 materials showed broad-band visible photoluminescence upon irradiation with ultraviolet light based on the charge transfer transition in the VO4(3-) units existing as dimers.