Fracture Strength After Fatigue Loading of Lithium Disilicate Pressed Zirconia Crowns

So-Yeun Kim, Jae-Won Choi, Sung-Won Ju

    The International Journal of Prosthodontics
    |August 2, 2016
    PubMed
    Abstract

    More Related Videos

    Oral Biofilm Formation on Different Materials for Dental Implants11:19

    Oral Biofilm Formation on Different Materials for Dental Implants

    Published on: June 24, 2018

    12.3K
    Fused Filament Fabrication FFF of Metal-Ceramic Components08:43

    Fused Filament Fabrication FFF of Metal-Ceramic Components

    Published on: January 11, 2019

    18.2K

    Related Concept Videos

    Fatigue01:21

    Fatigue

    Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
    975
    Stress-Strain Diagram - Brittle Materials01:24

    Stress-Strain Diagram - Brittle Materials

    Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
    4.8K
    Yield Criteria for Ductile Materials under Plane Stress01:25

    Yield Criteria for Ductile Materials under Plane Stress

    In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
    The Maximum Shearing Stress Criterion, also known as...
    651
    Fatigue Strength of Concrete01:22

    Fatigue Strength of Concrete

    Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
    649
    Stress-Strain Diagram - Ductile Materials01:24

    Stress-Strain Diagram - Ductile Materials

    The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...
    2.4K