Preparation and characterization of a degradable magnesium phosphate bone cement
Ying Yu1, Chao Xu1, Honglian Dai2
1State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, PR China.
Abstract:
A kind of degradable magnesium phosphate bone cement (MPBC) was fabricated by using the mixed powders of magnesium oxide (MgO), potassium dihydrogen phosphate (KH2PO4) and calcium dihydrogen phosphate (Ca(H2PO4)2.H2O). As MgKPO4, the main product of MgO and KH2PO4 was alkaline, the Ca(H2PO4)2.H2O was added to neutralize the alkali of the system. And the effects of Ca(H2PO4)2.H2O on the performance of MPBC were discussed. The results showed that the adding of Ca(H2PO4)2.H2O extended the setting time, which was about 6 min to 18 min. The compressive strength increased first and then decreased, and maximum value reached 31.2 MPa after setting for 24 h without any additional pressure. The MPBC was degradable in Tris-HCl solution, and the extracts of the cytotoxicity assay showed that the MPBC had good biocompatibility, indicating that the MPBC had good biodegradable and biocompatible properties.