Synthesis of MXene/Ag Composites for Extraordinary Long Cycle Lifetime Lithium Storage at High Rates

A new MXene/Ag composite was synthesized by direct reduction of a AgNO3 aqueous solution in the presence of MXene (Ti3C2(OH)0.8F1.2). The as-received MXene/Ag composite can be deemed as an excellent anode material for lithium-ion batteries, exhibiting an extraordinary long cycle lifetime with a large capacity at high charge-discharge rates. The results show that Ag self-reduction in MXene solution is related to the existence of low-valence Ti. Reversible capacities of 310 mAh·g(-1) at 1 C (theoretical value being ∼320 mAh·g(-1)), 260 mAh·g(-1) at 10 C, and 150 mAh·g(-1) at 50 C were achieved. Remarkably, the composite withstands more than 5000 cycles without capacity decay at 1-50 C. The main reasons for the long cycle life with high capacity are relevant to the reduced interface resistance and the occurrence of Ti(II) to Ti(III) during the cycle process.