Surface Modification of Li-Rich Cathode Materials for Lithium-Ion Batteries with a PEDOT:PSS Conducting Polymer
Feng Wu1,2, Jianrui Liu1, Li Li1,2
1School of Materials Science & Engineering, Beijing Key Laboratory of Environmental Science and Engineering, Beijing Institute of Technology , Beijing 100081, China.
Abstract:
Composites of lithium-rich Li1.2Ni0.2Mn0.6O2 and poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (
Pedot:
PSS) are synthesized through coprecipitation followed by a wet coating method. In the resulting samples, the amorphous conductive polymer films on the surface of the Li1.2Ni0.2Mn0.6O2 particles are 5-20 nm thick. The electrochemical properties of Li1.2Ni0.2Mn0.6O2 are obviously enhanced after
Pedot:
PSS coating. The composite sample with an optimal 3 wt % coating exhibits rate capability and cycling properties that are better than those of Li1.2Ni0.2Mn0.6O2, with an excellent initial discharge capacity of 286.5 mA h g(-1) at a current density of 0.1 C and a discharge capacity that remained at 146.9 mA h g(-1) at 1 C after 100 cycles. The improved performances are ascribed to the high conductivity of the
Pedot:
PSS coating layer, which can improve the conductivity of the composite material. The
Pedot:
PSS layer also suppresses the formation and growth of a solid electrolyte interface. Surface modification with
Pedot:
PSS is a feasible approach for improving the comprehensive properties of cathode materials.