Electrospun cellulose acetate phthalate nanofibrous scaffolds fabricated using novel solvent combinations...

Electrospun nanofibres have been shown to exhibit extracellular matrix (ECM)-like characteristics required for tissue engineering in terms of porosity, flexibility, fibre organization and strength. This study focuses on developing novel cellulose acetate phthalate (CAP) scaffolds by electrospinning for establishing 3-D chondrocyte and neuronal cultures. Five solvent combinations were employed in fabricating the fibres, namely, acetone/ethanol (9:1), dimethylformamide/tetrahydrofuran/acetone (3:3:4), tetrahydrofuran/acetone (1:1), tetrahydrofuran/ethanol (1:1) and chloroform/methanol (1:1). The electrospun fibres were characterized by scanning electron microscopy (SEM) analysis and confirmed to be within the nanometre range. Based on the morphology of the fibers from SEM results, two solvent combinations such as acetone/ethanol and dimethylformamide/tetrahydrofuran/acetone were selected for stabilization as CAP exhibits a pH dependent solubility. Fourier-Transform Infrared (FTIR) analysis revealed the hydrolysis of CAP which was overcome by EDC [1-ethyl-3-(3-dimethylaminopropyl) carbodiimide] and EDC/NHS (N-hydroxysuccinimide) cross-linking resulting in its stability (pH of 7.2) for three months. MTT [3-(4, 5-dimethylthiazol-2-yl)-1, 5-diphenyltetrazolium bromide] assay performed using L6 myoblast confirmed the biocompatibility of the scaffolds. 3-D primary chondrocyte and neuronal cultures were established on the scaffolds and maintained for a period of 10 days. H&E staining and SEM analysis showed the attachment of the chondrocytes and neurons on CAP scaffolds prepared using dimethylformamide/tetrahydrofuran/acetone and acetone/ethanol respectively.