Enhanced upconversion emission in crystallization-controllable glass-ceramic fiber containing Yb(3+)-Er(3+) codoped
Wencai Peng1, Zaijin Fang, Zhijun Ma
1State Key Laboratory of Luminescent Materials and Devices, Guangdong Engineering Technology Research and Development Center of Special Optical Fiber Materials and Devices, South China University of Technology, Guangzhou 510640, People's Republic of China.
Abstract:
Functional nanocrystal-containing materials have been a hot topic in recent years. However, few researches have focused on functional nanocrystals contained in optical glass fibers. In this research, transparent CaF2 glass-ceramic was prepared by a melt-quenching method. Greatly enhanced upconversion luminescence was observed after heat treatment. By applying a novel method called melt-in-tube, precursor fiber free of crystals was fabricated at the drawing temperature where the clad was softened while the core was melted. Glass-ceramic fiber with fiber core containing Yb(3+)-Er(3+) codoped CaF2 nanocrystals was obtained after heat treatment at a relatively low temperature. Electron probe micro-analyzer measurement shows no obvious element diffusion between the core and clad. Greatly enhanced upconversion emission was detected in the glass-ceramic fiber excited by a 980 nm laser, suggesting the developed glass-ceramic fiber is a promising material for upconversion laser.