Enamel shear bond strength of two orthodontic self-etching bonding systems compared to Transbond™ XT

The aim of this in vitro study was to compare the shear bond strength (SBS) and Adhesive Remnant Index (ARI) scores of two self-etching no-mix adhesives (Prompt L-Pop™ and Scotchbond™) for orthodontic appliances to the commonly used total etch system Transbond XT™ (in combination with phosphoric acid).

In all, 60 human premolars were randomly divided into three groups of 20 specimens each. In group 1 (control), brackets were bonded with Transbond™ XT primer. Prompt L-Pop™ (group 2) and Scotchbond™ Universal (group 3) were used in the experimental groups. Lower premolar brackets were bonded by light curing the adhesive. After 24 h of storage, the shear bond strength (SBS) was measured using a Zwicki 1120 testing machine. The adhesive remnant index (ARI) was determined under 10× magnification. The Kruskal-Wallis test was used to statistically compare the SBS and the ARI scores.

No significant differences in the SBS between any of the experimental groups were detected (group 1: 15.49 ± 3.28 MPa; group 2: 13.89 ± 4.95 MPa; group 3: 14.35 ± 3.56 MPa; p = 0.489), nor were there any significant differences in the ARI scores (p = 0.368).

Using the two self-etching no-mix adhesives (Prompt L-Pop™ and Scotchbond™) for orthodontic appliances does not affect either the SBS or ARI scores in comparison with the commonly used total-etch system Transbond™ XT. In addition, Scotchbond™ Universal supports bonding on all types of surfaces (enamel, metal, composite, and porcelain) with no need for additional primers. It might therefore be helpful for simplifying bonding in orthodontic procedures.