Controlled synthesis and magnetic properties of iron-cobalt-phosphide nanorods
Weiwei Yang1, Xiaoming Wu, Yongsheng Yu
1State Key Laboratory of Urban Water Resource and Environment, Harbin Institute of Technology, Harbin 150090, China. ysyu@hit.edu.cn.
Abstract:
A simple one-step solution-phase synthesis of iron-cobalt-phosphide ((Fe1-xCox)2P) nanorods (NRs) is reported in this paper. Through the control of the amount of Co in the samples, the crystal structure of (Fe1-xCox)2P NRs changes from a pure Fe-rich hexagonal Fe2P type structure to a mixture of Fe-rich hexagonal Fe2P and Co-rich orthorhombic Co2P type structures. These samples show superparamagnetic behavior at room temperature and ferromagnetic properties at 10 K. When the Co composition is 0.09, the (Fe0.91Co0.09)2P sample has the highest coercivity around 5.74 kOe at 10 K. The current route provides a new and general chemical method for tunable preparation of (Fe1-xCox)2P (x < 0.28) NRs, which are significant for the development of new iron- or cobalt-rich permanent magnet materials without rare-earth or noble metals.
More Related Videos
08:40Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production
Published on: December 6, 2021
10:45Stable Aqueous Suspensions of Manganese Ferrite Clusters with Tunable Nanoscale Dimension and Composition
Published on: February 5, 2022
Related Concept Videos
01:31Ferromagnetism
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human...