Enhancing the efficiency of thiomers: Utilizing a highly mucoadhesive polymer as backbone for thiolation and...

The objective of this study was to develop a novel thiomer with enhanced mucoadhesive properties using a highly mucoadhesive polymeric backbone. Fixomer™ A-30 (poly(methacrylic acid-co-sodium acrylamidomethyl propane sulfonate)), exhibiting a mucoadhesive strength superior to that of all other polymers, was thiolated by conjugation with l-cysteine and furthermore preactivated with 2-mercaptonicotinic acid (MNA). The resulting derivatives Fix-SH and Fix-S-MNA exhibited coupling rates of 755μmol thiol groups and 304μmol MNA per gram polymer, respectively. The mucoadhesive profile was evaluated with three different methods: tensile studies, rotating cylinder and rheological synergism. In tensile studies, a total work of adhesion of above 500μJ was determined for the unmodified polymer that increased to around 750μJ after thiolation and around 1500μJ after preactivation. The adhesion time of Fix-SH on the rotating cylinder was 3.7-fold and that of Fix-S-MNA 6.8-fold longer compared to the unmodified polymer. A rheological synergism was observed for the unmodified polymer as well as the derivatives with a non-significant difference for Fix-SH but a 5.44-fold improvement for Fix-S-MNA. Fix-S-MNA showed a significantly improved swelling behavior with a water-uptake up to the 30-fold of its initial weight over >50h whereas thiolation showed only slight improvements. Derivatization had no significant influence on cell viability. According to the results, Fix-S-MNA seems to be a suitable polymer for mucoadhesive drug delivery systems.