Effect of pre-heating on the mechanical properties of silorane-based and methacrylate-based composites
Narmin Mohammadi1, Elmira Jafari-Navimipour1, Soodabeh Kimyai2
1Associate professor at the Operative Dentistry Department, Dental and Periodontal Research Center, Faculty of Dentistry, Tabriz University of Medical Sciences, Tabriz, Iran.
Background:
The use of composites in dental restoration has been commonly criticized, due to their underwhelming mechanical properties. This problem may be solved partially by preheating. The present research aims to determine the effect of preheating on the mechanical properties of two different classes of composites.
Material And Methods:
A Silorane-based (Silorane) and a Methacrylate-based (Z250) composite were preheated to different temperatures (25, 37, and 68 °C) and afterwards were tested with the appropriate devices for each testing protocol. The material's flexural strength, elastic modulus, and Vickers microhardness were evaluated. Two-way ANOVA, and Tukey's post hoc were used to analyze the data.
Results:
Microhardness and elastic modulus increased with preheating, while flexural strength values did not increase significantly with preheating. Furthermore the methacrylate-based composite (Z250) showed higher values compared to the Silorane-based composite (Silorane) in all the tested properties.
Conclusions:
Preheating Silorane enhances the composite's microhardness and elastic modulus but does not affect its flexural strength. On the other hand, preheating Z250 increases its microhardness but does not change its flexural strength or elastic modulus. In addition, the Z250 composite shows higher microhardness and flexural strength than Silorane, but the elastic modulus values with preheating are similar. Therefore Z250 seems to have better mechanical properties making it the better choice in a clinical situation. Key words:Composite, elastic modulus, flexural strength, microhardness, preheating.