Effects of four different phosphorus-locking materials on sediment and water quality in Xi'an moat

To lower phosphorus concentration in Xi'an moat, four different phosphorus-locking materials, namely, calcium nitrate, sponge-iron, fly ash, and silica alumina clay, were selected in this experiment to study their effects on water quality and sediment. Results of the continuous 68-day experiment showed that calcium nitrate was the most effective for controlling phosphorus concentration in overlying and interstitial water, where the efficiency of locking phosphorus was >97 and 90 %, respectively. Meanwhile, the addition of calcium nitrate caused Fe/Al-bound phosphorus (Fe/Al-P) content in sediment declining but Ca-bound phosphorus (Ca-P) and organic phosphorus (OP) content ascending. The phosphorus-locking efficiency of sponge-iron in overlying and interstitial water was >72 and 66 %, respectively. Meanwhile, the total phosphorus (TP), OP, Fe/Al-P, and Ca-P content in sediment increased by 33.8, 7.7, 23.1, and 23.1 %, respectively, implying that under the action of sponge-iron, the locked phosphorus in sediment was mainly inorganic form and the phosphorus-locking efficiency of sponge-iron could be stable and persistent. In addition, the phosphorus-locking efficiency of fly ash was transient and limited, let alone silica alumina clay had almost no capacity for phosphorus-locking efficiency. Therefore, calcium nitrate and sponge-iron were excellent phosphorus-locking agents to repair the seriously polluted water derived from an internal source.