Dual color emitting Eu doped strontium orthosilicate phosphors synthesized by bio-template assisted ultrasound for...

A novel Sr₂SiO₄:Eu (1-5mol %) superstructures (SS) were synthesized using bio-sacrificial A.V. gel assisted ultrasound method. Powder X-ray diffraction patterns confirmed the presence of both α and β phase formation. It was evident that the morphological growth was highly reliant on A.V. gel concentration, sonication time, pH and sonication power. The formation mechanisms for different hierarchical SS were proposed. From diffuse reflectance spectra, the energy band gap was estimated and found to be ∼4.70-5.11eV. The photoluminescence emission spectra for the excitation at 392nm, shows characteristic emission peaks at 593, 613, 654 and 702nm which were attributed to ⁵D₀→⁷F₀, ⁷F_1,⁷F₂ and ⁷F₃ transitions of Eu³⁺ ions respectively. Conversely, when the samples were subjected to the heat treatment at 850°C for 3h under argon atmosphere, display an intense broad emission peak with two de-convoluted peaks at 490 and 550nm due to 4f⁶5d¹→4f¹ (⁸S_7/2) transitions of Eu²⁺ ions. The concentration quenching phenomenon was discussed which attributes to energy transfer, electron-phonon coupling and ion-ion interaction. The Judd-Ofelt intensity parameters and other radiative properties were estimated by using emission spectra. The CIE chromaticity coordinate values of Sr₂SiO₄:Eu²⁺ and Eu³⁺ nanophosphors were located in green and red regions respectively. The calculated CCT and CRI values specify that the present phosphor can be fairly useful for both green and red components of white LED's. Luminescence decay and quantum yield suggest the suitability of this phosphor as an efficient luminescent medium for light emitting diodes. Overall, the results elucidated a rapid, environmentally benign, cost-effective and convenient method for Sr₂SiO₄:Eu³⁺ synthesis and for the possible applications such as solid state lighting and display devices.