Shear bond strength of veneering ceramic to coping materials with different pre-surface treatments

Natasya Ahmad Tarib1, Norsamihah Anuar2, Marlynda Ahmad3

  • 1Department of Prosthodontic, Faculty of Dentistry, Universiti Kebangsaan Malaysia, Kuala Lumpur, Malaysia.

The Journal of Advanced Prosthodontics
|November 10, 2016
PubMed
Abstract

Keywords:
Lithium disilicateMetal alloyPre-surface treatmentShear bond strengthZirconiadental bondingsurface treatmentprosthetic materialsshear strength

More Related Videos

Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives08:40

Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives

Published on: May 17, 2020

3.5K
Preparation and Testing of Plant Seed Meal-based Wood Adhesives08:09

Preparation and Testing of Plant Seed Meal-based Wood Adhesives

Published on: March 5, 2015

9.1K

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
546
Veneer01:19

Veneer

Veneer refers to a thin sheet of wood, typically produced to a thickness of about one-eighth of an inch or less. This material is crafted through various methods, the most common being rotary cutting. In this process, a log is mounted into a large lathe and spun against a knife edge, peeling off a continuous strip of wood as the knife penetrates deeper into the rotating log, creating a rotary-cut veneer.
Other veneering techniques include plain-slicing, quarter-slicing, and rift-slicing. These...
453
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
521
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
545
Mortar Joint Deterioration in Masonry01:13

Mortar Joint Deterioration in Masonry

Mortar joint deterioration is a significant concern in masonry structures, with water accumulation in the joints leading to damage from freeze-thaw cycles. The repeated expansion of water during freezing and its melting during thawing develop and propagate cracks in the masonry joints. Eventually, this leads to the spalling of mortar from the joints, loosening masonry units and weakening the structure. The deteriorated mortar joints are also vulnerable to moisture intrusion into the walls.
The...
392
Mortar Joints in Brick Masonry01:25

Mortar Joints in Brick Masonry

Mortar joints play a critical role in brick masonry, filling the spaces between brick to bind them together and provide structural integrity and strength. The thickness of these joints is variable, typically ranging from less than one-fourth inch to over half an inch, based on structural needs and specific applications.
The process of joint tooling is implemented as the mortar begins to harden. This technique involves compacting and shaping the mortar to enhance both the appearance and the...
496