Synthesis of monodisperse spherical core-shell SiO₂-SrAl₂Si₂O₈: Eu²⁺ phosphors by hydrothermal homogeneous...

Nanocrystalline SrAl₂Si₂O₈ :Eu²⁺ phosphor layers were coated on nonaggregated, monodisperse and spherical SiO₂ particles using a hydrothermal homogeneous precipitation. After annealing at 1100 °C, core-shell SiO₂@SrAl₂Si₂O₈ :Eu²⁺ particles were obtained. They were characterized with x-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy and photoluminescence techniques. XRD analysis confirmed the formation of SiO₂ @SrAl₂Si₂O₈ :Eu²⁺ particles; it indicated that the SrAl₂Si₂O₈ :Eu²⁺ shells on SiO₂ particles consisted of hexagonal crystallites. The core-shell phosphors obtained are well-dispersed submicron spherical particles with a narrow size distribution. The thickness of the coated layer is approximately 20-40 nm. Under ultraviolet excitation (361 nm), the particles emit blue light at about 440 nm due to the Eu²⁺ ions in their shells.