The development of Ce³⁺-activated (Gd,Lu)₃Al₅O₁₂ garnet solid solutions as efficient yellow-emitting phosphors

Ce³⁺-activated Gd₃Al₅O₁₂ garnet, effectively stabilized by Lu³⁺ doping, has been developed for new yellow-emitting phosphors. The powder processing of [(Gd_1- Lu ) Ce ]₃Al₅O₁₂ solid solutions was achieved through precursor synthesis via carbonate precipitation, followed by annealing. The resultant (Gd,Lu)AG:Ce³⁺ phosphor particles exhibit typical yellow emission at ∼570 nm (5d-4f transition of Ce³⁺) upon blue-light excitation at ∼457 nm (the ²F_5/2-5d transition of Ce³⁺). The quenching concentration of Ce³⁺ was determined to be ∼1.0 at% (y = 0.01) and the quenching mechanism was suggested to be driven by exchange interactions. The best luminescent [(Gd_0.9Lu_0.1)_0.99Ce_0.01]AG phosphor is comparative to the well-known YAG:Ce³⁺ in emission intensity but has a substantially red-shifted emission band that is desired for warm-white lighting. The effects of processing temperature (1000-1500 °C) on the spectroscopic properties of the phosphors, especially those of Lu³⁺/Ce³⁺, were thoroughly investigated and discussed from the centroid position and crystal field splitting of the Ce³⁺ 5d energy levels.