A novel method for synthesis of α-Si₃N₄ nanowires by sol-gel route

Silicon nitride (Si₃ N₄) nanowires have been prepared by carbothermal reduction followed by the nitridation (CTRN) of silica gel containing ultrafine excess carbon obtained by the decomposition of dextrose over the temperature range of 1200-1350 °C. This innovative process involves repeated evacuation followed by purging of nitrogen gas so that the interconnected nanopores of the gel are filled with nitrogen gas prior to heat treatment. During heat treatment at higher temperatures, the presence of nitrogen gas in the nanopores of the gel starts the CTRN reaction simultaneously throughout the bulk of the gel, leading to the formation of Si₃ N₄ nanowires. The in situ generated ultrafine carbon obtained by the decomposition of dextrose decreases the partial pressure of oxygen in the system to stabilize the nanowires. The nanowires synthesized by this process are of ∼500 nm diameter and ∼0.2 mm length. The product was characterized by scanning electron microscope (SEM), energy dispersive x-ray analysis (EDX), x-ray diffraction (XRD) and infrared (IR) spectra.