Micro-/nanofibers prepared via co-assembly of paclitaxel and dextran
Tongtong Zhou1, Bangshang Zhu2, Feng Chen3
1Instrumental Analysis Center, Shanghai Jiao Tong University, 200240 Shanghai, China; State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University, 201620 Shanghai, China; State Key Laboratory of Metal Matrix Composites, School of Chemistry and Chemical Engineering, Shanghai Jiao Tong University, 200240 Shanghai, China.
Abstract:
In this paper, we reported the preparation of micro-/nanofibers via co-assembly with paclitaxel (PTX) and dextran (DEX). The co-assembly fibers formed in PTX and DEX mixture solution via non-covalent interactions including hydrophilic/hydrophobic interactions and π-π stacking. The micro-/nanofibers could be obviously observed when the mixed solution became turbid and ivory-white in color. The properties of fibers were characterized by SEM, TEM, FTIR, DSC, XRD, in vitro release and MTT assay. The length of fibers could reach several centimeters. The diameter of microfibers and nanofibers was about 800nm and 80nm, respectively. In addition, the PTX loading efficiency was over 78% in co-assembly fibers and up to 84% when PTX and DEX (Mw: 40,000) both were 2mg/mL. The sustained drug release and low cytotoxicity in vitro of PTX/DEX fibers were also demonstrated. Therefore, we believe that PTX/DEX micro-/nanofibers would have great potential for drug delivery of PTX.