Adsorption behavior of levulinic acid onto microporous hyper-cross-linked polymers in aqueous solution: Equilibrium,...

The recovery of levulinic acid (LA) from aqueous solution and actual biomass hydrolysate by a microporous hyper-cross-linked polymer, SY-01, was investigated for the first time under batch and fixed-bed column conditions. The results showed that the optimum pH should be in the acidic range (pH < 3.0) without adjusting the pH. In the single-component system equilibrium study, the Langmuir isotherm model fits the LA adsorption onto SY-01 resin better than the Freundlich isotherm model, indicating that LA adsorption onto SY-01 resin under the concentration range studied is a monolayer homogeneous adsorption process. The maximum adsorption capacity of LA onto SY-01 resin decreased with increasing temperature, ranging from 103.74 to 95.70 mg/g. The obtained thermodynamic parameters suggested that the adsorption of LA on SY-01 was spontaneous (ΔG⁰<-3.788 kJ/mol), and exothermic (ΔH⁰ = -11.764 kJ/mol). For kinetic study, the adsorption of LA onto SY-01 resin at various operating conditions follows the pore diffusion model and the intraparticle diffusion is the rate-limiting step for the adsorption of LA onto SY-01 resin. The effective pore diffusivity was dependent upon temperature, but independent of initial LA concentration, and were 3.306 × 10^-10, 5.274 × 10^-10 and 7.707 × 10^-10 m²/s at 298, 318 and 338 K, respectively. In desorption process, the recovery efficiency of LA from SY-01 resin was 99.39%, and LA concentration in the eluent was raised 2.97-fold. In conclusion, our results show that the SY-01 resin has potential application in product recovery of LA from biomass hydrolysate.