Single-step synthesis of crystalline h-BN quantum- and nanodots embedded in boron carbon nitride films

Herein we report on the synthesis and characterization of novel crystalline hexagonal boron nitride (h-BN) quantum- and nanodots embedded in large-area boron carbon nitride (BCN) films. The films were grown on a Cu substrate by an atmospheric pressure chemical vapour deposition technique. Methane, ammonia, and boric acid were used as precursors for C, N and B to grow these few atomic layer thick uniform films. We observed that both the size of the h-BN quantum/nanodots and thickness of the BCN films were influenced by the vaporization temperature of boric acid as well as the H₃BO_{3 (g)} flux over the Cu substrate. These growth conditions were easily achieved by changing the position of the solid boric acid in the reactor with respect to the Cu substrate. Atomic force microscope (AFM) and TEM analyses show a variation in the h-BN dot size distribution, ranging from nanodots (∼224 nm) to quantum dots (∼11 nm) as the B-source is placed further away from the Cu foil. The distance between the B-source and the Cu foil gave an increase in the C atomic composition (42 at% C-65 at% C) and a decrease in both B and N contents (18 at% B and 14 at% N to 8 at% B and 7 at% N). UV-vis absorption spectra showed a higher band gap energy for the quantum dots (5.90 eV) in comparison with the nanodots (5.68 eV) due to a quantum confinement effect. The results indicated that the position of the B-source and its reaction with ammonia plays a significant role in controlling the nucleation of the h-BN quantum- and nanodots. The films are proposed to be used in solar cells. A mechanism to explain the growth of h-BN quantum/nanodots in BCN films is reported.