Reducing Hysteresis and Enhancing Performance of Perovskite Solar Cells Using Low-Temperature Processed Y-Doped SnO₂...

Despite the rapid increase of efficiency, perovskite solar cells (PSCs) still face some challenges, one of which is the current-voltage hysteresis. Herein, it is reported that yttrium-doped tin dioxide (Y-SnO₂ ) electron selective layer (ESL) synthesized by an in situ hydrothermal growth process at 95 °C can significantly reduce the hysteresis and improve the performance of PSCs. Comparison studies reveal two main effects of Y doping of SnO₂ ESLs: (1) it promotes the formation of well-aligned and more homogeneous distribution of SnO₂ nanosheet arrays (NSAs), which allows better perovskite infiltration, better contacts of perovskite with SnO₂ nanosheets, and improves electron transfer from perovskite to ESL; (2) it enlarges the band gap and upshifts the band energy levels, resulting in better energy level alignment with perovskite and reduced charge recombination at NSA/perovskite interfaces. As a result, PSCs using Y-SnO₂ NSA ESLs exhibit much less hysteresis and better performance compared with the cells using pristine SnO₂ NSA ESLs. The champion cell using Y-SnO₂ NSA ESL achieves a photovoltaic conversion efficiency of 17.29% (16.97%) when measured under reverse (forward) voltage scanning and a steady-state efficiency of 16.25%. The results suggest that low-temperature hydrothermal-synthesized Y-SnO₂ NSA is a promising ESL for fabricating efficient and hysteresis-less PSC.