Effect of mold diameter on the depth of cure of a resin-based composite material

The purpose of this study was to examine the effect of mold diameter on depth of cure of a resin-based composite material for varying amounts of irradiation. A resin-based composite was light-cured for 10-80 s in stainless-steel molds of either 6 mm or 4 mm in diameter and then dark-stored for 24 h. Specimens were then scraped back and the length of the cured specimens was measured to provide depth of cure (D_SB ). Radiant exposure to each of the mold diameters was determined by measuring the power. The D_SB values using the 4-mm molds were lower than those of the 6-mm molds. The average difference between the two groups for each irradiation time was 0.45 ± 0.02 mm. A fixed depth of cure required about 39% more irradiation time for the 4-mm mold than for the 6-mm mold but 75% more radiant exposure. The difference in cure depth for a fixed radiant exposure was 0.79 mm. A better comparison of depth of cure is obtained by using identical radiant exposures for different mold diameters. It is believed that greater loss of light by absorption at the stainless-steel cylinder walls for the 4-mm-diameter cylinders accounts for the lower depth of cure when compared with the 6-mm molds.