Nanoscale zero-valent iron supported by biochars produced at different temperatures: Synthesis mechanism and effect
Linbo Qian1, Wenying Zhang1, Jingchun Yan1
1Key Laboratory of Soil Environment and Pollution Remediation, Institute of Soil Science, Chinese Academy of Sciences, Nanjing 210008, Jiangsu Province, China.
Abstract:
Biochar-supported nanoscale zero-valent iron (nZVI) produced under different temperatures was studied to evaluate the effect of the nZVI-biochar composite on the removal of hexavalent chromium (Cr(VI)) in solution. The structure of biochar-supported nZVI and its roles in Cr(VI) removal were investigated by X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR) and batch experiments. The XRD revealed that the removal rate of Cr(VI) for the nZVI supported by rice straw pyrolyzed at 400 °C (RS400) was much greater than that for other supporting biochar, and the FTIR further indicated that the carboxyl groups and silicon mineral within the biochar served as dual support sites for nZVI. NZVI-RS400 exhibited the highest removal amount of Cr(VI) at approximately 40.0 mg/g under an initial pH of 4.0, possibly due to both the reduction and adsorption processes. Therefore, the RS400-supported nanoscale zero-valent iron could be a preferable material for Cr(VI)-contaminated groundwater.
More Related Videos
10:44Preparation of Biomass-based Mesoporous Carbon with Higher Nitrogen-/Oxygen-chelating Adsorption for CuII Through Microwave Pre-Pyrolysis
Published on: February 12, 2019
08:40Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production
Published on: December 6, 2021