Spinel-type manganese ferrite (MnFe₂O₄) microspheres: A novel affinity probe for selective and fast enrichment of...

The spinel-type magnetic manganese ferrite (MnFe₂O₄) microspheres synthesized by simple solvothermal method were used as a novel adsorbent for selective enrichment and effective isolation of phosphopeptides. The uniform MnFe₂O₄ magnetic affinity microspheres (MAMSs) had a narrow particle size distribution between 250 and 260nm, and displayed superparamagnetism with a saturation magnetization value of 67.0emu/g. Comprehensively, the possible formation mechanism of MnFe₂O₄ microspheres with ferric and manganous sources as dual precursors was elucidated by comparison with those of Fe₃O₄ nanoparticles and MnOOH nanosheets respectively with either ferric or manganous source as single precursor. It was suggested that the spherical or sheet nanostructures could be achieved via secondary recrystallization or Ostwald ripening. The MnFe₂O₄ MAMSs probe exhibited excellent dispersibility in aqueous solution, and rapid magnetic separation within 15s, as well as good reusability. More importantly, MnFe₂O₄ was highly selective for phosphopeptides because of the strong coordination interaction between metal ions (Fe³⁺ and Mn²⁺) and phosphate groups of phosphopeptdies. This high specificity was demonstrated by effectively enriching phosphopeptides from digest mixture of β-casein and bovine serum albumin (BSA) with high content of non-phosphopeptides, and embodied further in phosphopeptides enrichment from non-fat milk digests and human serum. Consequently, the prepared MnFe₂O₄ affinity materials are expected to possess great potential in phosphoproteome research.