Ageing behavior of extruded Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr (wt.%) alloy containing LPSO phase and γ' precipitates

C Xu1,2, T Nakata2, X G Qiao1

  • 1School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, PR China.

Scientific Reports
|February 24, 2017
PubMed

More Related Videos

Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography06:53

Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography

Published on: January 25, 2019

15.2K
Processing of Bulk Nanocrystalline Metals at the US Army Research Laboratory08:58

Processing of Bulk Nanocrystalline Metals at the US Army Research Laboratory

Published on: March 7, 2018

9.9K

Related Concept Videos

Washing, Drying, and Ignition of Precipitates00:52

Washing, Drying, and Ignition of Precipitates

After filtration, the precipitate is washed to remove coprecipitated impurities and any remaining mother liquor. Colloidal precipitates, such as silver chloride, are washed with an electrolyte (such as dilute nitric acid) to prevent the peptization of the precipitate. In the case of slightly soluble precipitates, the wash solution contains a common ion to reduce solubility. Lead sulfate, which is slightly soluble in water, is washed with dilute sulfuric acid. Similarly, wash solutions may be...
6.9K
Ziegler–Natta Chain-Growth Polymerization: Overview01:17

Ziegler–Natta Chain-Growth Polymerization: Overview

Ziegler–Natta polymerization is another form of addition or chain‐growth polymerization used for synthesizing linear polymers over branched polymers. The catalyst used for polymerization is the Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, who developed it in 1953. This catalyst is an organometallic complex of titanium tetrachloride and triethyl aluminum, with the active form of the catalyst being an alkyl titanium compound. Using the Ziegler–Natta...
4.1K